MVLDPE

MVLDPE DOWLEX™ 2045G STYRON US

374

Unit Price:US$ 1,320 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength
Application Areas:film
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity		ASTM D1003	10 %
gloss		ASTM2457	60
turbidity	50.8um	ASTM D-1003	10 %
gloss	45°，50.8um	ASTM D-2457	60

Other performance	Test Condition	Test Method	Test Result
impact force		ASTM D882	4241 ft-lbf/in3
impact force	impact force		ASTM D882	4176 ft-lbf/in3
Elmendorf tear strength		ASTM D1922	23.6 g/micron
Elmendorf tear strength	Elmendorf tear strength		ASTM D1922	17.8 g/micron
Film toughness	50.8um，TD	ASTM D-882	351 J/cm4
Film toughness	Film toughness	50.8um，MD	ASTM D-882	346 J/cm³
Thin film puncture strength	50.8um	Internal Method	19.4 J/cm³

machinability	Test Condition	Test Method	Test Result
Melt Temperature			232 °C

Basic Performance	Test Condition	Test Method	Test Result
density		ASTM D-792	0.92 g/m3
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	1 g/10min
film thickness			50.8 um

mechanical properties	Test Condition	Test Method	Test Result
Secant modulus	2% Secant，50.8um，MD	ASTM D-882	194 Mpa
Secant modulus	Secant modulus	2% Secant，50.8um，TD	ASTM D-882	233 Mpa
tensile strength	50.8um，Yield,MD	ASTM D-882	10.9 Mpa
tensile strength	tensile strength	50.8um，Yield,TD	ASTM D-882	12.3 Mpa
Dart impact		ASTM D1709	288 g
Elmendorf tear strength		ASTM D192	1200 g
Elmendorf tear strength	Elmendorf tear strength		ASTM D192	902 g
elongation	Break	ASTM D882	889 %
elongation	elongation	Break	ASTM D882	827 %
impact force			235 ft-lbf/in3
Elongation at Break	50.8um，MD	ASTM D-882	830 %
Elongation at Break	Elongation at Break	50.8um，TD	ASTM D-882	890 %
tensile strength	50.8um，MD,Break	ASTM D-882	49.8 Mpa
	tensile strength	50.8um，TD,Break	ASTM D-882	55.1 Mpa
		tensile strength		ASTM D882	10.89 Mpa
		tensile strength	tensile strength		ASTM D882	12.29 Mpa
Secant modulus		ASTM D882	194.4 Mpa
Secant modulus	Secant modulus		ASTM D882	232.6 Mpa
tensile strength		ASTM D882	55.11 Mpa
tensile strength	tensile strength		ASTM D882	49.81 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM1525	108 °C
Vicat softening temperature	Vicat softening temperature	Melting Temperature	陶氏化学方法(DSC	122 °C
Melting temperature		Internal Method	122 °C
Vicat softening temperature		ASTM D-1525	108 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	℃/Kg	ASTM D1238	1.0 g/10min
melt mass-flow rate	melt mass-flow rate	厚度		50.8 microns

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

MVLDPE DOWLEX™ 2045G STYRON US

Material Description

Technical Data Sheet Compare

Technical Data Sheet