PC/ABS

PC/ABS INFINO® NH-1015B K23608 LOTTE KOREA

354

Unit Price:US$ 2,695 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜transparent
Application Areas:Home appliance applications｜Laptop
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	44 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	775 °C
UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	2.0mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/50	2500 Mpa
tensile strength	Yield	ASTM D638	62.0 Mpa
	tensile strength	Yield	ISO 527-2/50	60.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	48.0 Mpa
Bending modulus		ASTM D790	2400 Mpa
Bending modulus	Bending modulus		ISO 178	2450 Mpa
bending strength		ASTM D790	86.0 Mpa
bending strength	bending strength		ISO 178	88.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B50	98.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	100 °C
RTI Elec	1.5mm	UL 746	90.0 °C
RTI Imp	1.5mm	UL 746	85.0 °C
RTI Str	1.5mm	UL 746	90.0 °C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	93.0 °C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	98.0 °C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	81.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	93.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0kg	ASTM D1238	23 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	23 g/10min

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	1.5mm	UL 746	PLC 3
Hot wire ignition	1.5mm	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS INFINO® NH-1015B K23608 LOTTE KOREA

Material Description

Technical Data Sheet Compare

Technical Data Sheet