Material Description

Material Properties:enhance｜environment?protection
Application Areas:Automotive Applications｜sporting goods
Color:--
Grade:Injection grade

Material Certification

MSDS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			40%加纤.增强.低光泽
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	45	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.28mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ASTM D256/ISO 179	11	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	45	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	1.6	%
tensile strength		ASTM D638/ISO 527	200	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	122
Bending modulus		ASTM D790/ISO 178	15.5	kg/cm²(MPa)[Lb/in²]
Taber abraser	1000Cycles	ISO 9352	50.0	mg
Friction coefficient			0.25
shear strength	23°C	JISK7214	75.0	Mpa
bending strength	23°C	ISO 178	290	Mpa
Bending modulus	23°C	ISO 178	15500	Mpa
Tensile strain	Break,23°C	ISO 527-2	1.6	%
tensile strength	23°C	ISO 527-2	200	Mpa
bending strength		ASTM D790/ISO 178	290	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.3E-05	cm/cm/°C
Melting temperature		ISO 11357-3	278	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	3.1E-05	cm/cm/°C
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	>260	℃（℉）
Melting temperature			278	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.3	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Shrinkage rate	MD:3.00mm4	Internal Method	0.20	%
Shrinkage rate	Shrinkage rate	TD:3.00mm3	Internal Method	0.80	%
density		ASTM D792/ISO 1183	1.66
Shrinkage rate		ASTM D955	0.2	%
Water absorption rate		ASTM D570/ISO 62	0.02	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Dielectric constant		ASTM D150/IEC 60250	3.6
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Dielectric constant	23°C,1MHz	IEC 60250	3.60
Dielectric strength		IEC 60243-1	25	KV/mm
Volume resistivity		IEC 60093	1E+16	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	122
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	150	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Baoyu Plastic	US$ 5200 /MT
Dongguan Zhifei	US$ 5460 /MT
Guangdong Harmony	US$ 6490 /MT

Supplier Join

Get App

Top

PPS Torelina® A504X95 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index