'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS FORTRON® 1140L4 SF3001 CELANESE USA
16
- Unit Price:US$ 7,590 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan Juheng Plastic Material Co., Ltd.
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High temperature resistance｜enhance｜Glass fiber reinforced｜Injection grade｜Medium melt viscosity
- Application Areas:Fiber grade｜During injection molding｜Slight flash
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| SpecificHeatCapacity of Melt | Internal Method | 1500 | J/kg/°C | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 53 | kJ/m² |
| 23°C | ISO 179/1eU | 53 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 10 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 47 | % | |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA | |
| 1.5mm | UL 94 | V-0 | ||
| 0.38mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.65 | g/cm³ | |
| Water absorption rate | ASTM-D570 | 0.02 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | ISO 527 | 195 | Mpa | |
| Tensile modulus | ISO 527 | 14700 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Bending modulus | ISO 178 | 14500 | Mpa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 10 | kJ/m² | |
| Rockwell hardness | ASTM-D785 | 100 | R-Scale | |
| tensile strength | Break,23°C | ASTM D638 | 200 | Mpa |
| Break | ISO 527-2/1A/5 | 195 | Mpa | |
| elongation | Break,23°C | ASTM D638 | 1.7 | % |
| Break | ISO 527-2/1A/5 | 1.9 | % | |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| bending strength | ISO 178 | 285 | Mpa | |
| Tensile modulus | -40°C | ASTM D638 | 14500 | Mpa |
| 75°C | ASTM D638 | 11900 | Mpa | |
| 150°C | ASTM D638 | 4270 | Mpa | |
| 200°C | ASTM D638 | 3240 | Mpa | |
| -- | ISO 527-2/1A/1 | 14700 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.80Mpa | ISO 75-A | 270 | °C |
| UL flame retardant rating | UL 94 | V-0 | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Annealed | ASTM D648 | 280 | °C |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| 1.8MPa,Unannealed | ASTM D648 | 265 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | ISO 294-4 | 0.2-0.6 | % | |
| TD | ISO 294-4 | 0.40-0.60 | % | |
| MD | ISO 294-4 | 0.20-0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Shrinkage rate | TD | ASTM D955 | 0.50-0.70 | % |
| MD | ASTM D955 | 0.20-0.30 | % | |
| Specific volume | ASTM D792 | 0.611 | cm³/g | |
| density | ASTMD792 | 1.65 | g/cm³ | |
| Biochemical properties | Test Condition | Test Method | Test Result | Test Unit |
| Filling amount | 40 | % | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | -- | ASTM D257 | 1E+16 | ohms·cm |
| -- | IEC 60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 28 | KV/mm | |
| Dielectric constant | 1kHz | ASTM D150 | 3.50 | |
| 1MHz | ASTM D150 | 3.50 | ||
| 1MHz | IEC 60250 | 4.60 | ||
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| 1MHz | ASTM D150 | 1E-03 | ||
| Compared to the anti leakage trace index | IEC 60112 | PLC 4 | ||
| Arc resistance | ASTM D495 | 134 | sec | |
| Dissipation factor | 1MHz | IEC 60250 | 6.2E-03 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 100 | |
| M-Sale | ISO 2039-2 | 100 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | Internal Method | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.