Material Properties:High rigidity｜Thermal stability｜Low viscosity and high barrier
Application Areas:Automotive Applications｜Aerospace Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M级	ASTM D785	114

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火,6.40mm	ASTM D648	210 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,6.40mm	ASTM D648	211 °C
vicat		ASTM D15255	226 °C
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	170 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.41mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.9mm	UL 94	5VA
Limiting Oxygen Index		ASTM D2863	50 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.20mm	ASTM D256	480 J/m

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6kg	ASTM D1238	9.0 g/10min

Electrical performance	Test Condition	Test Method	Test Result
arc resistance		ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 4
High arc combustion index (HAI)	HAI	UL 746	PLC 4
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 2
Hot wire ignition (HWI)	HWI	UL 746	PLC 1

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	6890 Mpa
tensile strength	断裂	ASTM D638	140 Mpa
elongation	断裂	ASTM D638	4.0 %
flexural modulus	100mmSpan	ASTM D790	6890 Mpa
bending strength	Break,100mmSpan	ASTM D790	228 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.