PEI

PEI ULTEM™ 9085-WH8E187 SABIC INNOVATIVE US

281

Unit Price:US$ 12,206 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Low toxicity｜Low smoke
Application Areas:Railway Applications｜national defense｜Profile｜Aircraft interior parts
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13 kJ/m²

flammability	Test Condition	Test Method	Test Result
FAAFlammability		FAR25.853	<5
Extreme Oxygen Index		ASTM D2863	49 %
OSU peak heat release rate		FAR25.853	36.0 kW/m²
OSU total heat release		FAR25.853	16.0 kW·min/m²
VerticalBurnTest	60s),passesat，Testa	FAR25.853	2.0 sec

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTM D638	7.0 %
tensile strength	Break	ISO 527-2/5	71.0 Mpa
	tensile strength	Break	ASTM D638	74.0 Mpa
		tensile strength	Yield	ISO 527-2/5	88.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	84.0 Mpa
Tensile modulus		ISO 527-2/1	3050 Mpa
Tensile modulus	Tensile modulus		ASTM D638	3440 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	138 Mpa
bending strength	bending strength		ISO 178	90.0 Mpa
Bending modulus		ISO 178	2750 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2920 Mpa
Tensile strain	Break	ISO 527-2/5	50 %
elongation	Break	ASTM D638	72 %
Tensile strain	Yield	ISO 527-2/5	6.7 %

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B120	173 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	152 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	153 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.17 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.39 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	65.5 cm3/10min
melt mass-flow rate	295°C/6.6kg	ASTM D1238	8.9 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.