Material Description

Material Properties:High impact resistance｜Weather resistance
Application Areas:Electrical appliances｜Electronic field｜Electrical field
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	220℃/10.0kg	ASTM D-1238	6.0 g/10min
melt mass-flow rate	melt mass-flow rate	220℃/10kg	ISO 1133	7.80 cm
Water absorption rate	Soultion	ISO 62	0.40 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	1100 MPa
Rockwell hardness		ASTM D-785	95 R-Scale
Impact strength of cantilever beam gap	23℃，6.35mm	ASTM D-256	294 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，3.18mm	ASTM D-256	395 J/m
Charpy Notched Impact Strength	23℃	ISO 179/1eU	No Break KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179/1eU	42.2 KJ/m
Tensile strain	Yield	ISO 527-2	5.0 %
tensile strength	Yield	ISO 527-2	39.0 MPa
tensile strength	tensile strength	Yield	ASTM D-638	39.3 MPa
bending strength		ASTM D-790	66.9 MPa
Bending modulus		ASTM D-790	1960 MPa
Tensile strain	Break	ISO 527-2	28 %
Tensile strain	Tensile strain	Break	ASTM D-638	35 %
Charpy Notched Impact Strength	23℃	ISO 179/1eA	50.2 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃	ISO 179/1eA	3.90 KJ/m

thermal performance	Test Condition	Test Method	Test Result
UL flame retardant rating	3.20mm	ISO 1210	HB
	UL flame retardant rating	3.18mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	1.59mm	UL 94	HB
Vicat softening temperature	50℃/h，B(50N)	ISO 306	93.8 ℃
Vicat softening temperature	Vicat softening temperature		ASTM D-1525	103 ℃
Glass transition temperature		ISO 11357-2	110 ℃
Hot deformation temperature	1.80MPa，Unannealed	ASTM D-648	91.1 ℃
Linear coefficient of thermal expansion	Transverse	ISO 11359-2	0.000094 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	0.000094 cm/cm/℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow	ASTM D-955	0.40-0.70 %
density		ASTM D-792	1.07
density	density		ISO 1183	1070 Kg/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ASA LI-913 LG CHEM KOREA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet