Material Description

Material Properties:Thermal stability｜Low flow
Application Areas:Architectural application field
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	2540μm	ASTM D1003	88.0to90.0	%
turbidity	2540μm	ASTM D1003	<0.80	%
Refractive index		ASTMD542	1.586
impact performance	Test Condition	Test Method	Test Result	Test Unit
23°C		ASTM D256	900	J/m
-30°C		ISO 180/1A	12	kJ/m²
23°C		ISO 180/1A	70	kJ/m²
23°C	23°C		ASTMD4812	无断裂
-30°C		ISO 180/1U	无断裂
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	65.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.60mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Yield, 50.0mm span		ASTM D790	90.0	Mpa
--8		ISO 178	90.0	Mpa
--7		ISO 178	2300	Mpa
50.0mm span		ASTM D790	2300	Mpa
crack		ISO 527-2/50	>70	%
crack	crack		ASTM D638	>70	%
yield		ISO 527-2/50	6.0	%
	yield		ASTM D638	6.0	%
		yield		ISO 527-2/50	63.0	Mpa
		yield	yield		ASTM D638	63.0	Mpa
--2		ASTM D638	2350	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity		ASTMC177	0.20	W/m/K
23 to 80 ° C		ISO 11359-2	7E-05	cm/cm/°C
-40 to 95 ° C		ASTME831	7E-05	cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature		ISO 306/B50	144	°C
0.45MPa, unannealed, 3.20mm		ASTM D648	138	°C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	138	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	127	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	127	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTMD792	1.20	g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.50	cm3/10min
Shrinkage rate	MD：--1	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Saturation, 23 ° C		ISO 62	0.35	%
Balance, 23 ° C		ASTM D570	0.35	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	ASTMD150	0.010
Dissipation factor	Dissipation factor	60Hz	ASTMD150	1E-03
Dielectric constant	1MHz	ASTMD150	3.00
Dielectric constant	Dielectric constant	60Hz	ASTMD150	3.00
Dielectric strength	1.60mm	ASTMD149	27	KV/mm
Volume resistivity		ASTMD257	>1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Hardness (Rockwell R)		ISO 2039-2	120
Hardness (Rockwell R)	Hardness (Rockwell R)		ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.