PC LEXAN™  EXL9414T-1T9A8054T SABIC INNOVATIVE NANSHA

181
  • Unit Price:US$ 3,808 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Low temperature and high ductility
  • Application Areas:Thin walled products
  • Color:--
  • Grade:--

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity2000 μmInternal Method84.0 %
turbidity2000 μmInternal Method3.0 %
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376375.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94V-1
UL flame retardant rating1.8 mmUL 94V-0
Extreme Oxygen IndexISO 4589-235 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--1ASTM D6382180 Mpa
Tensile modulus--ISO 527-2/12300 Mpa
tensile strengthYield2ASTM D63857.0 Mpa
tensile strengthYieldISO 527-2/5056.0 Mpa
tensile strengthBreak2ASTM D63859.0 Mpa
tensile strengthBreakISO 527-2/5055.0 Mpa
elongationYield2ASTM D6385.6 %
elongationYieldISO 527-2/505.4 %
elongationBreak2ASTM D638120 %
elongationBreakISO 527-2/50110 %
Bending modulus50.0 mm Span3ASTM D7902180 Mpa
Bending modulus--4ISO 1782120 Mpa
bending strength--4,5ISO 17888.0 Mpa
bending strengthYield, 50.0 mm Span3ASTM D79092.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8ISO 75-2/Af116 °C
Vicat softening temperature--ASTM D15259138 °C
Vicat softening temperature--ISO 306/B120139 °C
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8316.7E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-26.7E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8318.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-28.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.090 %
Water absorption rateSaturation, 23°CISO 620.12 %
Shrinkage rate3.20 mm，FlowInternal Method0.40 - 0.80 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113312.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123813 g/10 min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.