PC LEXAN™ EXL1414-BK10227L SABIC INNOVATIVE US

Unit Price:US$ 3,450 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Guangdong Zecheng New Material Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
Application Areas:Bottle cap｜Home appliance components｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	65	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ASTM D256	770	J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	870	J/m
		Impact strength of cantilever beam gap	-30°C8	ISO 180/1A	60	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C8	ISO 180/1A	70	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	70.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	0.8 mm	IEC 60695-2-12	850	°C
UL flame retardant rating	0.40 mm	UL 94	HB
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875	°C
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2020	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2150	Mpa
tensile strength	Yield3	ASTM D638	55.0	Mpa
	tensile strength	Yield	ISO 527-2/50	57.0	Mpa
		tensile strength	Break3	ASTM D638	50.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	60.0	Mpa
elongation	Yield3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break3	ASTM D638	98	%
		elongation	elongation	Break	ISO 527-2/50	120	%
Bending modulus	50.0 mm Span4	ASTM D790	2230	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2250	Mpa
bending strength	--5,6	ISO 178	85.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	92.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature in the middle of the barrel			280 to 305	°C
Temperature at the rear of the barrel			270 to 295	°C
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the front of the material cylinder			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Processing (melt) temperature			295 to 315	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Exhaust hole depth			0.025 to 0.076	mm
Screw speed			40 to 70	rpm
drying temperature			120	°C
drying time			3.0 to 4.0	hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	125	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	140	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	124	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	128	°C
Vicat softening temperature	--	ASTM D152510	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	146	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
density	--	ASTM D792	1.18	g/cm³
density	density	--	ISO 1183	1.19	g/cm³
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	100 Hz	ASTM D150	2.68
Dielectric strength	0.800 mm, in Oil	ASTM D149	16	KV/mm
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Dissipation factor	1 MHz	ASTM D150	9.3E-3
Dissipation factor	Dissipation factor	100 Hz	ASTM D150	1.2E-3
Dielectric constant	1 MHz	ASTM D150	2.64
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L -Sale	ASTM D785	89
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3450 /MT

Supplier Join

Get App

Top

PC LEXAN™ EXL1414-BK10227L SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index