Material Description

  • Material Properties:Flame retardant
  • Application Areas:Bottle capCasters
  • Color:--
  • Grade:Injection grade

Technical Data Sheet Compare

hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM 级ASTM D78570
Rockwell hardnessR 级ASTM D785118
thermal performanceTest ConditionTest MethodTest Result
Heat Deflection Temperature0.45 MPa, 未退火, 6.40 mmASTM D648137 °C
Heat Deflection Temperature1.8 MPa, 未退火, 6.40 mmASTM D648132 °C
vicatASTM D15255154 °C
Linear coefficient of thermal expansion-40 到 95°C,流动ASTM E8316.8E-5 cm/cm/°C
specific heatASTM C3511260 J/kg/°C
thermal conductivityASTM C1770.29 W/m/K
RTI ElecUL 746130 °C
RTI ImpUL 746130 °C
RTIUL 746130 °C
optical performance Test ConditionTest MethodTest Result
refractive indexASTM D5421.586
transmissivity2540 µmASTM D100388.0 %
Haze ratio2540 µmASTM D10031.0 %
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75 mmUL 94V-2
UL flame retardant rating6.0 mmUL 94V-0
Impact resistanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
Dart impact23°CASTM D3029169 J
Impact strength of cantilever beam gapASTM D1822546 kJ/m²
Physical propertiesTest ConditionTest MethodTest Result
Specific volumeASTM D7920.830 cm³/g
melt mass-flow rate300°C/1.2 kgASTM D12387.0 g/10 min
shrinkage rate3.20 mm,Flow内部方法0.50 - 0.70 %
Water absorption rate24 hrASTM D5700.15 %
Water absorption rate平衡, 23°CASTM D5700.35 %
Water absorption rate平衡, 100°CASTM D5700.58 %
Outdoor applicabilityUL 746Cf1
Electrical performanceTest ConditionTest MethodTest Result
volume resistivityASTM D257> 1.0E+17 ohms·cm
dielectric strength3.20 mm, in AirASTM D14915 KV/mm
dielectric constant60 HzASTM D1503.17
dielectric constant50 kHzASTM D1503.17
dielectric constant1 MHzASTM D1502.96
Dissipation Factor50 HzASTM D1509.0E-4
Dissipation Factor60 HzASTM D1509.0E-4
Dissipation Factor1 MHzASTM D1500.010
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
High arc combustion index (HAI)UL 746PLC 1
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 2
Hot wire ignition (HWI)UL 746PLC 4
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel290 to 310 °C
Temperature in the middle of the barrel300 to 320 °C
Temperature at the front of the material cylinder310 to 330 °C
Spray nozzle temperature305 to 325 °C
Processing (melt) temperature310 to 330 °C
mold temperature80 to 115 °C
Back pressure0.300 to 0.700 Mpa
screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
mechanical propertiesTest ConditionTest MethodTest Result
tensile strength屈服ASTM D63862.0 Mpa
tensile strength断裂ASTM D63865.0 Mpa
elongation屈服ASTM D6387.0 %
elongation断裂ASTM D638110 %
flexural modulus50.0 mm 跨距ASTM D7902340 Mpa
bending strength屈服, 50.0 mm 跨距ASTM D79093.0 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮ASTM D104410.0 mg
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.