thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm, 注塑	ASTM D648	210 °C
melting temperature		ASTM D3418	220 °C
Linear coefficient of thermal expansion	流动	ASTM D696	3.0E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	23°C, 3.20 mm, 注塑，Flow	ASTM D955	0.30 - 0.70 %
Water absorption rate	24 hr, 23°C	ASTM D570	0.60 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity	23°C	ASTM D257	1.0E+16 ohms·cm
dielectric strength	23°C, 1.00 mm	ASTM D149	25 KV/mm
dielectric constant	23°C, 1 MHz	ASTM D150	4.00

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 100 °C
drying time			4.0 to 5.0 hr
Temperature at the rear of the barrel			260 to 270 °C
Temperature in the middle of the barrel			270 to 285 °C
Temperature at the front of the material cylinder			270 to 290 °C
Spray nozzle temperature			270 to 295 °C
Processing (melt) temperature			270 to 295 °C
mold temperature			80 to 110 °C
Back pressure			29.4 to 58.8 Mpa
screw speed			30 to 60 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	196 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	3.0 %
flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	11800 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	275 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.