PA66

PA66 Leona™ 90G55 BK ASAHI JAPAN

269

Unit Price:US$ 2,906 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
77.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Weather resistance｜Good appearance｜High rigidity｜Glass fiber reinforced｜high strength
Application Areas:Automotive External Parts
Color:--
Grade:Weather resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	82 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	--	ASTM D790	15700 Mpa
elongation	Break, 23°C	ISO 527-2	2.0 %
elongation	elongation	Break	ASTM D638	2.0 %
tensile strength	--	ASTM D638	221 Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	232 Mpa
Tensile modulus	23°C	ISO 527-2	18600 Mpa
bending strength	23°C	ISO 178	394 Mpa
bending strength	bending strength	--	ASTM D790	348 Mpa
Bending modulus	23°C	ISO 178	15400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	225 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	240 °C
thermal conductivity			0.30 W/m/K
specific heat			1930 J/kg/°C
Linear coefficient of thermal expansion	Flow	ASTM D696	2.0E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	-- %
Water absorption rate	Water absorption rate	Saturation, 23°C		-- %
Shrinkage rate	Flow	Internal Method	0.20 %
Shrinkage rate	Shrinkage rate	横向Flow	Internal Method	0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		ASTM D149	28 KV/mm
Compared to the anti leakage trace index	3.00 mm	IEC 60112	V
Surface resistivity		ASTM D257	1.0E+13 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	120
	Rockwell hardness	M -Sale	ISO 2039-2	95
		Rockwell hardness	R-Scale	ASTM D785	120
		Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.