PC/ABS WONDERLOY® PC-365KZ ZHENJIANG CHIMEI

356

Unit Price:US$ 2,800 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
Lianyungang port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜heat-resisting｜Flame retardant
Application Areas:Automotive sector｜Electrical field｜Electronic field｜currency
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179	45	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	50	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	50	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180	45	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	80.0	Mpa
bending strength	bending strength	23°C	ASTM D790	78.5	Mpa
Bending modulus		ISO 178	2200	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	2260	Mpa
Tensile strain	Break	ISO 527-2/50	120	%
Tensile strain	Tensile strain	Break,23°C	ASTM D638	85	%
tensile strength	Break	ISO 527-2/50	50.0	Mpa
	tensile strength	Yield	ISO 527-2/50	54.0	Mpa
	tensile strength	tensile strength	Yield,23°C	ASTM D638	53.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/A50	138	°C
	Vicat softening temperature	--	ASTM D152511	125	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D152510	136	°C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	102	°C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	115	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	106	°C
Vicat softening temperature	--	ISO 306/B50	127	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 2577	0.40-0.60	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	0.40-0.60	%
Spiral flow length		Internal Method	30.0	CM
melt mass-flow rate	260°C/5.0kg	ISO 1133	20	g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ASTM D1238	20	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity		IEC 60093	1E+18	ohms·cm
Dielectric constant	1MHz	IEC 60250	3.10
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	115
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ASTM D785	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Xinfei Plastic	US$ 2870 /MT

Supplier Join

Get App

Top

PC/ABS WONDERLOY® PC-365KZ ZHENJIANG CHIMEI

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index