Mechanical properties	Test Method	Test Result
Impact strength of cantilever beam gap	ASTM D-256	85 J/m
elongation at break	ASTM D-638	1.4 %
bending strength	ASTM D-790	177 Mpa
tensile strength	ASTM D-638	132 Mpa
Flexural modulus	ASTM D-790	15200 Mpa
Impact strength of cantilever beam gap	ASTM D256/ISO 179	85 kg·cm/cm(J/M)ft·lb/in
elongation at break	ASTM D638/ISO 527	1.4 %
tensile strength	ASTM D638/ISO 527	132 kg/cm²(MPa)[Lb/in²]
Flexural modulus	ASTM D790/ISO 178	15200 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	177 kg/cm²(MPa)[Lb/in²]

Other performance	Test Condition	Test Method	Test Result
Grade @ Thickness		UL 746-B	V-0
Thickness Tested		UL 94	1.5 mm

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.77

Thermal performance	Test Condition	Test Method	Test Result
Temperature range for molding			30-95 °C
RTI Imp		UL 746-B	220 °C
	RTI Imp		UL 746-B	240 °C
	RTI Imp	RTI Imp		UL 746-B	240 °C
Glass Transition Temperature		ASTM D-3418	120 °C
RTI Elec		UL 746-B	240 °C
RTI Imp		UL 746-B	210 °C
drying temperature			135 °C
melting temperature		ASTM D-3418	335 °C
RTI Elec		UL 746-B	240 °C
Heat distortion temperature		ASTM D-648	272 °C
melting temperature			350-360 °C
Heat distortion temperature		ASTM D648/ISO 75	272 ℃（℉）
melting temperature			335 ℃（℉）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.