Material Properties:Flame retardant｜Glass fiber reinforced｜ Glass fiber reinforced by 30%｜Filler: Glass fiber reinforced material｜Flame retardant grade｜30%｜Filler by weight｜halogen-containing ｜Flame retardant grade｜30% filler by weight｜halogen-containing
Application Areas:Office supplies｜Automotive sector｜building materials｜Electronic field｜Electrical field
Color:--
Grade:Enhanced level
Technical Data Sheet
Other performance
Test Condition
Test Method
Test Result
filler content
无水｜30 wt%
filler content
1.3%水｜- wt%
impact performance
Test Condition
Test Method
Test Result
Charpy Notched Impact Strength
-40°C
kJ/m²
7.0 --
Charpy Notched Impact Strength
23°C
kJ/m²
9.5 14
Impact strength of simply supported beam without notch
23°C
kJ/m²
65 70
flammability
Test Condition
Test Method
Test Result
UL flame retardant rating
0.40mm
V-0 --
Basic Performance
Test Condition
Test Method
Test Result
Water absorption rate
23℃，24hr
ASTM D-570
无水｜0.4 %
Water absorption rate
23℃，24hr
ASTM D-570
1.3%水｜- %
mechanical properties
Test Condition
Test Method
Test Result
Impact strength of cantilever beam gap
23℃，Unnotched1/8
无水｜65 kg.cm/cm
Impact strength of cantilever beam gap
23℃，Unnotched1/8
1.3%水｜70 kg.cm/cm
tensile strength
23℃，Break
ASTM D-638
无水｜1640 kg/cm2
tensile strength
23℃，Break
ASTM D-638
1.3%水｜1350 kg/cm2
Elongation at Break
23℃
ASTM D-638
无水｜5 %
Elongation at Break
23℃
ASTM D-638
1.3%水｜5 %
bending strength
23℃
ASTM D-790
无水｜2490 kg/cm2
bending strength
23℃
ASTM D-790
1.3%水｜2000 kg/cm2
Bending modulus
23℃
ASTM D-790
无水｜93200 kg/cm2
Bending modulus
23℃
ASTM D-790
1.3%水｜65000 kg/cm2
Tensile strain
Break,-40°C
%
2.5 --
Tensile strain
Break,23°C
%
3.0 3.0
Tensile strain
Break,80°C
%
4.5 --
Bending modulus
-40°C
MPa
10200 --
Bending modulus
23°C
MPa
9300 6500
Bending modulus
80°C
MPa
5500 --
bending strength
-40°C
MPa
275 --
bending strength
23°C
250 MPa
bending strength
80°C
MPa
150 --
Taber abraser
1000Cycles
mg
26.0 --
tensile strength
-40°C
MPa
190 --
tensile strength
23°C
165 MPa
tensile strength
80°C
MPa
110 --
thermal performance
Test Condition
Test Method
Test Result
Linear coefficient of thermal expansion
ASTM D-696
无水｜2 10-5cm/cm.℃
Linear coefficient of thermal expansion
ASTM D-696
1.3%水｜-
Hot deformation temperature
18.6kg/cm2
ASTM D-648
无水｜251 °C
Hot deformation temperature
18.6kg/cm2
ASTM D-648
1.3%水｜- °C
Melting temperature
差示扫描测热计DSC法
265 °C
UL-94 flame retardant grade
UL 94
无水｜V-0
UL-94 flame retardant grade
UL 94
1.3%水｜-
Hot deformation temperature
0.45MPa,Unannealed
°C
251 --
Melting temperature
°C
265 --
Linear coefficient of thermal expansion
MD
cm/cm/°C
2E-05 --
Physical properties
Test Condition
Test Method
Test Result
density
ASTM D-792
无水｜1.59
density
ASTM D-792
1.3%水｜-
density
23°C
g/cm³
1.59 --
Shrinkage rate
TD:3.00mm3
%
0.60-0.90 --
Shrinkage rate
MD:3.00mm4
%
0.20-0.50 --
Water absorption rate
23°C,24hr
%
0.60 --
Water absorption rate
Saturation,23°C
%
4.0 --
Electrical performance
Test Condition
Test Method
Test Result
Volume resistivity
ASTM D-257
1.3%水｜8×1013 Ω.cm
Dielectric strength
1/8"
ASTM D-149
无水｜38 KV/mm
Dielectric strength
1/8"
ASTM D-149
1.3%水｜33 KV/mm
Compared to the Leakage Traceability Index (CTI)
UL 746
无水｜200 V
Compared to the Leakage Traceability Index (CTI)
UL 746
1.3%水｜- V
Dissipation factor
106Hz
ASTM D-150
无水｜0.003-0.009
Dissipation factor
106Hz
ASTM D-150
1.3%水｜-
Arc resistance
1/8"
ASTM D-495
无水｜70-80 S
Arc resistance
1/8"
ASTM D-495
1.3%水｜- S
Volume resistivity
ASTM D-257
无水｜8×1014 Ω.cm
Volume resistivity
ohms·cm
1E+15 1E+13
Dielectric strength
kV/mm
38 33
Dielectric constant
23°C,1kHz
4.00 --
Dielectric constant
23°C,1MHz
0.0100 --
Arc resistance
sec
70.0 --
Compared to the anti leakage trace index
CTI
V
PLC 3
hardness
Test Condition
Test Method
Test Result
Rockwell hardness
R-Sale,23°C
121 --
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)