ASA/PC GELOY™ HRA170-BK2G008 SABIC INNOVATIVE SHANGHAI
321
- Unit Price:US$ 2,727 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:90MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜heat-resisting｜High impact resistance
- Application Areas:Automotive sector｜Outdoor applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 106 Mpa |
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 112 °C | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 121 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| Burning wire flammability index | 3.20mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ISO 4589-2 | 22 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| -30°C | ISO 180/1A | 15 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| -30°C | ISO 179/1eA | 12 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 17.0 cm3/10min |
| shrinkage rate | MD1 | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.013 |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| fracture | ISO 527-2/5 | 130 % | |
| yield | ISO 527-2/50 | 4.0 % | |
| ISO 527-2/5 | 5.0 % | ||
| fracture | ISO 527-2/50 | 62.0 Mpa | |
| ISO 527-2/5 | 60.0 Mpa | ||
| yield | ISO 527-2/50 | 62.0 Mpa | |
| ISO 527-2/5 | 55.0 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 95.0 mg |
| bending strength | ISO 178 | 85.0 Mpa | |
| flexural modulus | ISO 178 | 2400 Mpa | |
| fracture | ISO 527-2/50 | >50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.