PC INFINO® SC-1222UR LOTTE KOREA

111

Unit Price:US$ 4,195 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.832mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--4	ISO 178	92.0	Mpa
bending strength	bending strength	--3	ASTM D790	90.0	Mpa
Bending modulus	--4	ISO 178	2300	Mpa
Bending modulus	Bending modulus	--3	ASTM D790	2300	Mpa
elongation	Break	ISO 527-2/50	110	%
elongation	elongation	Break2	ASTM D638	110	%
tensile strength	Break	ISO 527-2/50	64.0	Mpa
	tensile strength	Break2	ASTM D638	63.0	Mpa
		tensile strength	Yield	ISO 527-2/50	64.0	Mpa
		tensile strength	tensile strength	Yield2	ASTM D638	63.0	Mpa
Tensile modulus	--	ISO 527-2/50	2300	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2300	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Hot air dryer			120	°C
Vacuum drying machine			120	°C
Hot air dryer			4.0	hr
Vacuum drying machine			4.0	hr
Suggested maximum moisture content			< 0.050	%
Temperature at the rear of the barrel			50 to 80	°C
Temperature in the middle of the barrel			250 to 270	°C
Temperature at the front of the material cylinder			270 to 300	°C
Spray nozzle temperature			300	°C
Mold temperature			80 to 120	°C
Injection pressure			6.37	Mpa
Back pressure			1.47	Mpa
Screw speed			120 to 130	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B50	145	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	123	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	125	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	136	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	136	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.50 - 0.70	%
	Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.50 - 0.70	%
		Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.50 - 0.70	%
		Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.50 - 0.70	%
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	20	g/10 min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC INFINO® SC-1222UR LOTTE KOREA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index