LCP ZENITE® 5145L GY001 CELANESE USA
212
- Unit Price:US$ 6,249 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 290 °C |
| melting temperature | ISO 11357-3 | 319 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 7.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| 1.5 mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 33 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt density | 内部方法 | 1.48 g/cm³ | |
| Thermal conductivity of melt | 内部方法 | 0.35 W/m/K | |
| Ejection Temperature | 265 °C | ||
| Specific Heat Capacity of Melt | 1500 J/kg/°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 0.50 % |
| 流量 | ISO 294-4 | 0.10 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 45 KV/mm | |
| relative permittivity | 1 MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.018 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 °C | ||
| drying time | 3.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Hopper temperature | 20 to 30 °C | ||
| Temperature at the rear of the barrel | 320 to 330 °C | ||
| Temperature in the middle of the barrel | 335 to 345 °C | ||
| Temperature at the front of the material cylinder | 335 to 345 °C | ||
| Spray nozzle temperature | 335 to 345 °C | ||
| Processing (melt) temperature | 325 to 345 °C | ||
| mold temperature | 80 to 120 °C | ||
| Back pressure | < 3.00 Mpa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 15000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 115 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.1 % |
| flexural modulus | 23°C | ISO 178 | 11000 Mpa |
| bending strength | 23°C | ISO 178 | 190 Mpa |
| compression stress | 1% 应变 | ISO 604 | 21.3 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.