PC LNP™ THERMOCOMP™ D151-701 SABIC INNOVATIVE NANSHA

Unit Price:US$ 9,720 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Shenzhen Jiuhe New Material Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Non chloro non bromine flame retardant
Application Areas:Electronic and Electrical Applications｜Plastic bag
Color:--
Grade:Flame retardant enhanced grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	710	J/m
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	22.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.300mm	UL 94	V-2
	UL flame retardant rating	0.400mm	UL 94	V-1
	UL flame retardant rating	UL flame retardant rating	0.600mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--6		ISO 178	133	Mpa
Fracture, 50.0mm span		ASTM D790	131	Mpa
--5		ISO 178	4010	Mpa
50.0mm span		ASTM D790	4070	Mpa
crack		ISO 527-2/5	3.6	%
	crack		ASTM D638	3.6	%
		crack		ISO 527-2/5	82.0	Mpa
		crack	crack		ASTM D638	83.0	Mpa
--1		ASTM D638	4400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7.7E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	121	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117	°C
Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	3.4E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTM D1238	14	g/10min
melt mass-flow rate	melt mass-flow rate	300°C/2.16kg	ASTM D1238	29	g/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.040	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.080	%
Shrinkage rate	TD:24hr	ASTM D955	0.30-0.50	%
Shrinkage rate	Shrinkage rate	MD:24hr	ASTM D955	0.30-0.50	%
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	27.0	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	13.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1.10GHz	Internal Method	3.07
	Dielectric constant	1.90GHz	Internal Method	3.06
		Dielectric constant	5.00GHz	Internal Method	3.06
		Dielectric constant	Dielectric constant	10.0GHz	Internal Method	3.05
Dissipation factor	1.10GHz	Internal Method	6.7E-03
	Dissipation factor	1.90GHz	Internal Method	6.5E-03
		Dissipation factor	5.00GHz	Internal Method	6.9E-03
		Dissipation factor	Dissipation factor	10.0GHz	Internal Method	6.9E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 5140 /MT
Dongguan Yushengxin	US$ 5520 /MT
Dongguan Colorful	US$ 5840 /MT

Supplier Join

Get App

Top

PC LNP™ THERMOCOMP™ D151-701 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index