PC LEXAN™ EXL1132T NA8A005T SABIC INNOVATIVE US
161
- Unit Price:US$ 4,890 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:74MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low temperature resistance｜Easy to process｜High mobility｜UV resistance
- Application Areas:Household appliances｜Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 17 g/10min | |
| Melt volume flow rate | ISO 1133 | 16.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.40-0.80 % | |
| 内部方法 | 0.40-0.80 % | ||
| Water absorption rate | ISO 62 | 0.35 % | |
| ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 95.0 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 850 °C | |
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2280 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | ASTM D638 | 58.1 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ASTM D638 | 58.7 Mpa | ||
| ISO 527-2/50 | 55.0 Mpa | ||
| elongation | ASTM D638 | 5.8 % | |
| Tensile strain | ISO 527-2/50 | 5.0 % | |
| elongation | ASTM D638 | 110 % | |
| Tensile strain | ISO 527-2/50 | 100 % | |
| Flexural modulus | ASTM D790 | 2320 Mpa | |
| ISO 178 | 2240 Mpa | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| ASTM D790 | 95.1 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 25 kJ/m² | |
| ISO 179/1eA | 60 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 20 kJ/m² | |
| ISO 180/1A | 55 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 69.6 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 7.2E-05 cm/cm/°C | |
| ISO 11359-2 | 7.5E-05 cm/cm/°C | ||
| ASTME831 | 7.6E-05 cm/cm/°C | ||
| ISO 11359-2 | 7.5E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 125 °C | |
| Heat distortion temperature | ASTM D648 | 137 °C | |
| ISO 75-2/Be | 136 °C | ||
| ASTM D648 | 124 °C | ||
| ISO 75-2/Ae | 125 °C | ||
| vicat | ASTM D152511 | 144 °C | |
| ISO 306/B50 | 144 °C | ||
| ISO 306/B120 | 145 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.