PA6 Ultramid® 8202 BASF KOREA
198
- Unit Price:US$ 5,131 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜high strength｜Oil resistant
- Application Areas:Helmet｜Automotive Applications｜Engine parts
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 1.2 % | ||
| Water absorption rate | ASTM D570 | 1.6 % | |
| ISO 62 | 1.6 % | ||
| ASTM D570 | 9.5 % | ||
| ISO 62 | 9.5 % | ||
| ASTM D570 | 2.7 % | ||
| ISO 62 | 2.7 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-2 | ||
| UL 94 | V-2 | ||
| UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D790 | 17.0 Mpa | |
| ISO 178 | 85.0 Mpa | ||
| Flexural modulus | ASTM D790 | 3010 Mpa | |
| ASTM D790 | 2830 Mpa | ||
| ASTM D790 | 500 Mpa | ||
| ASTM D790 | 350 Mpa | ||
| ASTM D790 | 305 Mpa | ||
| ISO 178 | 2400 Mpa | ||
| bending strength | ASTM D790 | 170 Mpa | |
| ASTM D790 | 108 Mpa | ||
| ASTM D790 | 30.0 Mpa | ||
| ASTM D790 | 20.0 Mpa | ||
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| ISO 527-2 | 485 Mpa | ||
| ISO 527-2 | 360 Mpa | ||
| ISO 527-2 | 290 Mpa | ||
| tensile strength | ASTM D638 | 126 Mpa | |
| ASTM D638 | 78.0 Mpa | ||
| ASTM D638 | 35.0 Mpa | ||
| ASTM D638 | 25.0 Mpa | ||
| ISO 527-2 | 126 Mpa | ||
| ISO 527-2 | 78.0 Mpa | ||
| ISO 527-2 | 35.0 Mpa | ||
| ISO 527-2 | 25.0 Mpa | ||
| ISO 527-2 | 20.0 Mpa | ||
| ASTM D638 | 75.0 Mpa | ||
| elongation | ASTM D638 | 4.0 % | |
| ASTM D638 | 42 % | ||
| ASTM D638 | 36 % | ||
| Tensile strain | ISO 527-2 | 4.0 % | |
| elongation | ASTM D638 | 55 % | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 51 kJ/m² | |
| ISO 179 | NoBreak | ||
| Dart impact | 内部方法 | 142 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+13 ohms·cm | |
| IEC 60093 | >1.0E+13 ohms·cm | ||
| dielectric strength | ASTM D149 | 22 KV/mm | |
| IEC 60243-1 | 37 KV/mm | ||
| dielectric constant | IEC 60250 | 3.50 | |
| IEC 60250 | 3.30 | ||
| Dissipation Factor | IEC 60250 | 0.010 | |
| IEC 60250 | 0.020 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Imp | UL 746 | 75.0 °C | |
| UL 746 | 75.0 °C | ||
| UL 746 | 75.0 °C | ||
| RTI Str | UL 746 | 85.0 °C | |
| UL 746 | 85.0 °C | ||
| UL 746 | 85.0 °C | ||
| Heat distortion temperature | ASTM D648 | 178 °C | |
| ISO 75-2/B | 150 °C | ||
| ASTM D648 | 65.0 °C | ||
| ISO 75-2/A | 60.0 °C | ||
| melting temperature | ASTM D3418 | 220 °C | |
| ISO 3146 | 220 °C | ||
| Linear coefficient of thermal expansion | ASTME831 | 8.3E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 125 °C | |
| UL 746 | 125 °C | ||
| UL 746 | 125 °C | ||
| UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.