PEI

PEI ULTEM™ 2200-7316 SABIC INNOVATIVE US

266

Unit Price:US$ 4,376 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
11.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Food contact
Application Areas:Wear resistant accessories｜chip
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	64 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D4812	480 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	3.20mm	ASTM D256	460 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.41mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.9mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	50 %
NBSSmokeDensity-Flaming,Ds,4min		ASTME662	1.30

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	6890 Mpa
tensile strength	Break	ASTM D638	131 Mpa
elongation	Break	ASTM D638	4.0 %
Bending modulus	100mmSpan	ASTM D790	6890 Mpa
bending strength	Break,100mmSpan	ASTM D790	228 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	170 °C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	210 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	210 °C
Vicat softening temperature		ASTM D15255	220 °C
Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	2.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.30-0.50 %
Water absorption rate	24hr	ASTM D570	0.19 %
Water absorption rate	Water absorption rate	Equilibrium,23°C	ASTM D570	1.1 %
density		ASTM D792	1.42 g/cm³
melt mass-flow rate	337°C/6.6kg	ASTM D1238	6.0 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	7E+16 ohms·cm
Dielectric strength	1.60mm,inOil	ASTM D149	26 KV/mm
Dielectric constant	1kHz	ASTM D150	3.50
Dissipation factor	1kHz	ASTM D150	1.5E-03
Dissipation factor	Dissipation factor	2.45GHz	ASTM D150	4.9E-03
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 4
High voltage arc tracing rate	HVTR	UL 746	PLC 2
Hot wire ignition	HWI	UL 746	PLC 1

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 2200-7316 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet