PA12 Pebax® Rnew® AESNO TL ARKEMA FRANCE
278
- Unit Price:US$ 16,927 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:14MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜Thermal stability
- Application Areas:Automotive Applications｜tubing
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 75 |
| 邵氏D,15秒 | ISO 868 | 69 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ASTM E1356 | 35.0 °C | |
| melting temperature | ISO 11357-3 | 180 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA12.EHL.22-010 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | NoBreak |
| 23°C | ISO 179 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23℃，50%RH | ASTM D570 | 0.80 % |
| Shore hardness | ASTM 785 | 106 | |
| Melt volume flow rate | 235°C/5.0kg | ISO 11357 | 8.00 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D638 | 68.9 Mpa |
| Elongation at break | ASTM D638 | 330 % | |
| flexural modulus | ASTM D790 | 1200 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 140 J/m | |
| Tensile modulus | ISO 527-2 | 1440 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 43.0 Mpa |
| 断裂 | ISO 527-2 | 50.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| 断裂 | ISO 527-2 | >200 % | |
| flexural modulus | ISO 178 | 1180 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.