PC/ABS

PC/ABS CYCOLOY™ CX7240U SABIC INNOVATIVE SHANGHAI

279

Unit Price:US$ 4,625 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High impact resistance｜High mobility
Application Areas:Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.60 mm	UL 94	V-1
		UL flame retardant rating	0.75 mm	UL 94	V-0
			UL flame retardant rating	1.5 mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	104 Mpa
bending strength	bending strength	--5,6	ISO 178	96.0 Mpa
Bending modulus	--5	ISO 178	2500 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2750 Mpa
elongation	Break	ISO 527-2/50	90 %
	elongation	Break3	ASTM D638	100 %
		elongation	Yield	ISO 527-2/50	4.0 %
		elongation	elongation	Yield3	ASTM D638	4.1 %
tensile strength	Break	ISO 527-2/50	50.0 Mpa
	tensile strength	Break3	ASTM D638	58.0 Mpa
		tensile strength	Yield	ISO 527-2/50	65.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	65.0 Mpa
Tensile modulus	--	ISO 527-2/1	2530 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2950 Mpa

injection	Test Condition	Test Method	Test Result
Suggested maximum moisture content			0.040 %
Suggested injection volume			40 to 80 %
drying temperature			90 °C
drying time			4.0 hr
Temperature at the rear of the barrel			260 to 300 °C
Temperature in the middle of the barrel			260 to 300 °C
Hopper temperature			60 to 80 °C
Temperature at the front of the material cylinder			265 to 300 °C
Spray nozzle temperature			265 to 300 °C
Processing (melt) temperature			270 to 300 °C
Mold temperature			60 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
		Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	93.0 °C
Vicat softening temperature	--	ASTM D152510	106 °C
	Vicat softening temperature	--	ISO 306/B50	110 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	113 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.3E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	6.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.4E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	5.4E-5 cm/cm/°C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI		UL 746	90.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	16 g/10 min

Electrical performance	Test Method	Test Result
Compared to the anti leakage trace index	UL 746	PLC 3
High arc combustion index	UL 746	PLC 0
Hot wire ignition	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.