PBT VALOX™ 457 SABIC INNOVATIVE US

277

Unit Price:US$ 5,028 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Filler: Glass fiber reinforced material｜six｜5% filler by weight
Application Areas:Plastic bag｜Automotive External Parts｜Electrical/Electronic Applications｜Home appliance components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	32 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	270 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.711mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.00mm	UL 94	5VA
Burning wire flammability index	1.00mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	3.00mm9	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.00mm	IEC 60695-2-13	750 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.00mm	IEC 60695-2-13	725 °C
Extreme Oxygen Index		ASTM D2863	32 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	79.3 Mpa
Bending modulus	50.0mmSpan	ASTM D790	3520 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	124 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	140 °C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	204 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	152 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	6.7E-05 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.44 g/cm³
Specific volume		ASTM D792	0.690 cm³/g
Shrinkage rate	MD1	Internal Method	0.60-0.80 %
	Shrinkage rate	MD2	Internal Method	0.80-1.0 %
		Shrinkage rate	TD3	Internal Method	0.70-0.90 %
		Shrinkage rate	Shrinkage rate	TD4	Internal Method	0.90-1.2 %
Water absorption rate	24hr	ASTM D570	0.060 %

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 3
Volume resistivity		ASTM D257	>5.5E+16 ohms·cm
Dielectric strength	1.60mm,inOil	ASTM D149	24 KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTM D149	18 KV/mm
Dielectric constant	100Hz	ASTM D150	3.50
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.40
Dissipation factor	100Hz	ASTM D150	2E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.020
Arc resistance		ASTM D495	PLC7
Compared to the anti leakage trace index	CTI	UL 746	PLC 3

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.