PC LNP™ STAT-KON™ DC-1002 BK SABIC INNOVATIVE US

171

Unit Price:US$ 5,188 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
24.3MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to form｜Easy to demould
Application Areas:Plastic bag｜Electrical appliances｜Electronic and Electrical Applications
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	32 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.3 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan	ASTM D790	158 Mpa
bending strength	bending strength		ISO 178	149 Mpa
Bending modulus		ISO 178	7440 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	7460 Mpa
Tensile strain	Break	ISO 527-2/5	7.3 %
elongation	Break	ASTM D638	7.5 %
tensile strength	Break	ISO 527-2/5	97.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	97.0 Mpa
Tensile modulus		ISO 527-2/1	10300 Mpa
Tensile modulus	Tensile modulus		ASTM D638	11100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	5.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	2.6E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	142 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	141 °C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	145 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	146 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.080 %
Shrinkage rate	TD：24hr	ASTM D955	0.40-0.60 %
Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.20-0.40 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1.0E+4to1.0E+6 ohms·cm
Surface resistivity		ASTM D257	1.0E+3to1.0E+5 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ STAT-KON™ DC-1002 BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet