PC Makrolon® 2805 021139 COVESTRO GERMANY
245
- Unit Price:US$ 2,624 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:110MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medium viscosity｜Medium viscosity｜For general injection molding
- Application Areas:Automotive Applications｜Electrical applications｜Industrial applications｜Used for industrial accessories｜Automotive electronic components｜Electronic and electrical accessories; ul certification
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | -- | ISO 1183 | 1200 kg/m2 |
| Water absorption rate | 23℃：50%rh，静态均衡值 | ISO 62 | 0.12 % |
| 在23℃水中，饱和值 | ISO 62 | 0.30 % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow wire ignition temperature (GWIT) | 3.0毫米 | IEC 60695-2-13 | 875 ℃ |
| 1.5毫米 | IEC 60695-2-13 | 875 ℃ | |
| Glow wire combustion index (GWFI) | 1.0毫米 | IEC 60695-2-12 | 930 ℃ |
| 1.5毫米 | IEC 60695-2-12 | 850 ℃ | |
| Limiting Oxygen Index | A溶液 | ISO 4589-2 | 27 % |
| UL flame retardant rating | 3.0毫米 | UL 94 | 级 |
| 厚度 | UL 94 | HB(2.5) 级 | |
| 1.5毫米 | UL 94 | V-2 级 | |
| Linear coefficient of thermal expansion | 23-55℃，流动 | ISO 11359-1-2 | 0.65 10-4/K |
| 23-55℃，垂直 | ISO 11359-1-2 | 0.65 10-4/K | |
| vicat | 50N；50℃/小时 | ISO 306 | 145 ℃ |
| Glass Transition Temperature | 10℃/毫米 | ISO 11357-1-2 | 145 ℃ |
| Specific properties of raw materials | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 1毫米 | ISO 13468-2 | 89 % |
| refractive index | 过程A | ISO 489 | 1.586 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Traceability Index (CTI) | 23℃/50%r.h 方法A | IEC 60112 | 250 等级 |
| volume resistivity | 23℃/50%r.h | IEC 60093 | 1E+14 Ohm.m |
| Surface Resistivity | 23℃/50%r.h | IEC 60093 | 1E+16 Ohm |
| dielectric strength | 23℃/50%r.h 1毫米 | IEC 60243-1 | 34 kv/毫米 |
| Dissipation Factor | 23℃/50%r.h 1MHz | IEC 60250 | 90 10-4 |
| dielectric constant | 23℃/50%r.h 1MHz | IEC 60250 | 3.0 -- |
| Dissipation Factor | 23℃/50%r.h 100Hz | IEC 60250 | 5 10-4 |
| dielectric constant | 23℃/50%r.h 100Hz | IEC 60250 | 3.1 -- |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 60*60*2；500bar，垂直 | ISO 294-4 | 0.7 % |
| 60*60*2；500bar，流动 | ISO 294-4 | 0.65 % | |
| melt mass-flow rate | 300℃；1.2kg | ISO 1133 | 9.5 cm3/(10分钟) |
| 250℃；2.16kg | ISO 1133 | -- cm3/(10分钟) |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 23℃/50%r.h，断裂 | ISO 6603-2 | 60 J |
| Maximum destructive power | 23℃/50%r.h | ISO 6603-2 | 5400 N |
| Impact strength of cantilever beam gap | 23℃/50%r.h ；3.2毫米 | kJ/m² | 参照ISO 180/1eA 85P(C) |
| Charpy Notched Impact Strength | 23℃/50%r.h ；3毫米 | kJ/m² | 参照ISO 179/1eA 75P(C) |
| 23℃/50%r.h | ISO 179/1eU | N kJ/m² | |
| flexural modulus | 23℃/50%r.h 2毫米/分钟 | ISO 179 | 2400 MPa |
| Tensile creep modulus | 23℃/50%r.h 1000小时 | ISO 899-1 | 1900 MPa |
| 23℃/50%r.h 1小时 | ISO 899-1 | 2200 MPa | |
| fracture strain | 23℃/50%r.h 5毫米/分钟 | ISO 527-1-2 | -- % |
| Breaking stress | 23℃/50%r.h 5毫米/分钟 | ISO 527-1-2 | -- MPa |
| Elongation at break | 23℃/50%r.h 50毫米/分钟 | ISO 527-1-2 | ＞50 % |
| Tensile strain | 23℃/50%r.h 50毫米/分钟，屈服 | ISO 527-1-2 | 6.1 % |
| Tensile stress | 23℃/50%r.h 50毫米/分钟，屈服 | ISO 527-1-2 | 66 MPa |
| Tensile modulus | 23℃/50%r.h 1毫米/分钟 | ISO 527-1-2 | 2400 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.