PA66 LNP™ LUBRICOMP™ RCL-4536 SABIC INNOVATIVE US

Unit Price:US$ 7,130 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Huizhou Rijing Chemical Technology Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Thermal stability
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	65	kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	9.90	J
Multi axis Instrumented Impact Energy		ISO 6603-2	2.85	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ASTM D638	201	Mpa
tensile strength	tensile strength	Break	ISO 527-2	228	Mpa
elongation	Break	ASTM D638	1.4	%
Tensile strain	Break	ISO 527-2	2.0	%
Bending modulus		ASTM D790	16400	Mpa
Bending modulus	Bending modulus		ISO 178	21300	Mpa
bending strength		ASTM D790	333	Mpa
bending strength	bending strength		ISO 178	354	Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.25
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.23
Tensile modulus		ASTM D638	29500	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	23100	Mpa
Wear factor	Washer	ASTM D3702Modified	6.00	10^-10in^5-min/ft-lb-hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	2.3E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	3.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	3.4E-05	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	254	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	244	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	245	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：24hr	ASTM D955	0.20	%
	Shrinkage rate	TD：24hr	ASTM D955	0.40	%
		Shrinkage rate	TD:24hr	ISO 294-4	0.43	%
		Shrinkage rate	Shrinkage rate	MD:24hr	ISO 294-4	0.15	%
Water absorption rate	24hr,50%RH	ASTM D570	0.93	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.4	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 7210 /MT

Supplier Join

Get App

Top

PA66 LNP™ LUBRICOMP™ RCL-4536 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index