PPS Torelina® A390M65 TORAY JAPAN

392

Unit Price:US$ 4,940 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
52.7MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Glass fiber reinforced
Application Areas:Casters｜Electrical applications｜sporting goods
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			低光泽.尺寸稳定
Color			黑
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	17	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.72mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ASTM D256/ISO 179	17	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	0.9	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	7	kg·cm/cm(J/M)ft·lb/in
Taber abraser	1000Cycles	ISO 9352	70.0	mg
Friction coefficient			0.30
shear strength	23°C	JISK7214	60.0	Mpa
bending strength	23°C	ISO 178	210	Mpa
Bending modulus	23°C	ISO 178	19500	Mpa
Tensile strain	Break,23°C	ISO 527-2	0.90	%
tensile strength	Yield,23°C	ISO 527-2	105	Mpa
tensile strength	tensile strength		ASTM D638/ISO 527	105	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	19.5	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	210	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.9E-05	cm/cm/°C
Melting temperature		ISO 11357-3	278	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	>260	℃（℉）
Melting temperature			278	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.9	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Shrinkage rate	MD:3.00mm4	Internal Method	0.25	%
Shrinkage rate	Shrinkage rate	TD:3.00mm2	Internal Method	0.50	%
density		ASTM D792/ISO 1183	1.99
Water absorption rate		ASTM D570/ISO 62	0.02	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Dielectric constant	23°C,1MHz	IEC 60250	5.30
Dielectric strength		IEC 60243-1	21	KV/mm
Volume resistivity		IEC 60093	1E+16	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	122
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	8.00	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPS Torelina® A390M65 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index