POM TENAC™ LT802 ASAHI JAPAN
246
- Unit Price:US$ 5,383 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low friction coefficient｜Homopolymer｜wear resistant｜Lubricity｜Anti creep｜high viscosity
- Application Areas:Engine parts｜Household goods｜Engineering accessories｜Shell
- Color:--
- Grade:Impact resistant grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 1.7 g/10min | |
| Linear coefficient of thermal expansion | TMA法 | 10 | |
| Heat Deflection Temperature | 1.82MPa | ASTM D648 | 125 °C |
| 0.45MPa | ASTM D648 | 172 °C | |
| UL flame retardant rating | UL 94 | HB | |
| Combustibility (rate) | UL 94 | HB | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 125 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 10 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 对金属有优异的耐摩擦和耐耗 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.2 % | |
| shrinkage rate | 平行方向 | 旭化成法 | 1.8-2.2 % |
| 垂直方向 | 旭化成法 | 1.8-2.2 % | |
| density | ASTM D792/ISO 1183 | 1.42 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 1.7 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | - | ASTM D785 | 120 R |
| wear resistance | ASTM D1044 | 13 | |
| tensile strength | ASTM D638 | 64 Mpa | |
| Elongation at break | ASTM D638 | 80 % | |
| bending strength | ASTM D790 | 91 Mpa | |
| flexural modulus | ASTM D790 | 2650 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 118 J/m | |
| Rockwell hardness | - | ASTM D785 | 92 M |
| tensile strength | ASTM D638/ISO 527 | 64 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 80 % | |
| Rockwell hardness | ASTM D785 | 92 | |
| flexural modulus | ASTM D790/ISO 178 | 2650 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 91 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.