ABS

ABS Terluran® GP-22 BASF GERMANY

401

Unit Price:US$ 1,658 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
70MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS HI-121H LG GUANGZHOU

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High rigidity｜Medium impact resistance
Application Areas:Shell｜TV casing｜small home appliances
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Huangdu Index		DIN 6167	13 YI

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	22 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	180 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	59 J/m
	Impact strength of cantilever beam gap	-18°C	ASTM D256	100 J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	300 J/m
			Impact strength of cantilever beam gap	-30°C	ISO 180/A	8.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	26 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus		ISO 527-2	2300 Mpa
tensile strength	Yield,23°C	ASTM D638	45.0 Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	45.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.6 %
elongation	Break	ASTM D638	2.6 %
Nominal tensile fracture strain	23°C	ISO 527-2	10 %
Bending modulus		ASTM D790	2300 Mpa
bending strength		ASTM D790	65.0 Mpa
bending strength	bending strength		ISO 178	65.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5to1.1E-4 cm/cm/°C
thermal conductivity		DIN 52612	0.17 W/m/K
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	90.6 °C
	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	104 °C
		Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	99.0 °C
			Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	77.8 °C
				Hot deformation temperature	1.8MPa,Annealed	ASTM D648	98.9 °C
				Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	94.0 °C
Vicat softening temperature	--	ISO 306/A50	105 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	96.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.22 %
density		ASTM D792	1.04 g/cm³
density	density		ISO 1183	1.04 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.5 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	19 g/10min
Melt Volume Flow Rate (MVR)	230°C/3.8kg	ASTM D1238	4.80 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	MD	ASTM D955	0.40-0.70 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40-0.70 %
Water absorption rate	Saturation,23°C	ASTM D570	1.0 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	1.0 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric constant	1.00mm,1MHz	ASTM D150	2.80
Relative permittivity	100Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.80
Dissipation factor	100Hz	IEC 60250	4.8E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	7.9E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	103
Ball Pressure Test		ISO 2039-1	97.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.