plas

PC Makrolon®  2458 COVESTRO SHANGHAI

374
  • Unit Price:US$ 3,451 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    87.8MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact resistanceHigh mobilityFlame retardantHigh temperature resistance
  • Application Areas:Fitness equipmentHousehold appliancesHousehold appliancesBottle cap
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexISO 4891.586
transmissivity1000μmISO 13468-289.0 %
transmissivity2000μmISO 13468-289.0 %
transmissivity3000μmISO 13468-288.0 %
transmissivity4000μmISO 13468-287.0 %
turbidity3000μmISO 14782<0.80 %
impact performanceTest ConditionTest MethodTest Result
Multi axis Instrumented Impact Energy23°CISO 6603-255.0 J
Multi axis Instrumented Peak Impact Force-30°CISO 6603-26000 N
Multi axis Instrumented Peak Impact Force23°CISO 6603-25100 N
Charpy Notched Impact Strength-30°C,Complete BreakISO 739114 kJ/m²
Charpy Notched Impact Strength23°C,Partial BreakISO 739165 kJ/m²
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739115 kJ/m²
Impact strength of cantilever beam gap23°C,Partial BreakISO 739165 kJ/m²
Multi axis Instrumented Impact Energy-30°CISO 6603-265.0 J
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-228 %
FlashIgnitionTemperatureASTM D1929480 °C
SelfIgnitionASTM D1929550 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/12400 Mpa
tensile strengthYield,23°CISO 527-2/5065.0 Mpa
tensile strengthBreak,23°CISO 527-2/5070.0 Mpa
Tensile strainYield,23°CISO 527-2/506.1 %
Tensile strainBreak,23°CISO 527-2/50130 %
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Tensile creep modulus1hrISO 899-12200 Mpa
Tensile creep modulus1000hrISO 899-11900 Mpa
Bending modulus23°CISO 1782350 Mpa
bending strength3.5%Strain,23°CISO 17873.0 Mpa
bending strength23°CISO 17897.0 Mpa
Bending strain23°CISO 1787.1 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B139 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A125 °C
Glass transition temperatureISO 11357-2146 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120146 °C
Ball Pressure Test138°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD:23to55°CISO 11359-26.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:23to55°CISO 11359-26.5E-05 cm/cm/°C
thermal conductivity23°CISO 83020.20 W/m/K
Physical propertiesTest ConditionTest MethodTest Result
density23°CISO 11831.20 g/cm³
Apparent densityISO 600.66 g/cm³
melt mass-flow rate300°C/1.2kgISO 113320 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113319.0 cm3/10min
Shrinkage rateTDISO 25770.50-0.70 %
Shrinkage rateMDISO 25770.50-0.70 %
Shrinkage rateTD:2.00mm3ISO 294-40.70 %
Shrinkage rateMD:2.00mm3ISO 294-40.65 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931E+16 ohms
Volume resistivity23°CIEC 600931E+16 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-134 KV/mm
Relative permittivity23°C,100HzIEC 602503.10
Relative permittivity23°C,1MHzIEC 602503.00
Dissipation factor23°C,100HzIEC 602505E-04
Dissipation factor23°C,1MHzIEC 602509E-03
Compared to the anti leakage trace indexSolutionAIEC 60112 V
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1115 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.