PET Rynite® 545 NC010 DUPONT USA
332
- Unit Price:US$ 3,511 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:146.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance|Glass fiber reinforced|High temperature resistance|Short fiber reinforcement
- Application Areas:Fiber grade
- Color:--
- Grade:Enhanced level
Material Certification

Technical Data Sheet
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
Rockwell hardness | ISO 2039-2 | 100 | |
ISO 2039-2 | 120 |
other | Test Condition | Test Method | Test Result |
---|---|---|---|
characteristic | 45%矿物/玻纤增强.强度和刚度.尺寸稳定性和抗蠕变 |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Combustibility (rate) | UL 94 | HB | |
Heat Deflection Temperature | ASTM D648/ISO 75 | 250 ℃(℉) | |
ASTM D648/ISO 75 | 226 ℃(℉) | ||
Effective thermal diffusivity coefficient | 1.4E-07 m²/s | ||
Heat Deflection Temperature | ISO 75-2/A | 226 °C | |
ISO 75-2/C | 180 °C | ||
vicat | ISO 306/B50 | 230 °C | |
melting temperature | ISO 11357-3 | 252 °C | |
Linear coefficient of thermal expansion | ISO 11359-2 | 1.5E-05 cm/cm/°C | |
ISO 11359-2 | 8.3E-05 cm/cm/°C | ||
thermal conductivity | 0.32 W/m/K |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
burning rate | ISO 3795 | <100 mm/min | |
UL flame retardant rating | UL 94 | HB | |
UL 94 | HB | ||
IEC 60695-11-10,-20 | HB | ||
IEC 60695-11-10,-20 | HB | ||
Limiting Oxygen Index | ISO 4589-2 | 20 % | |
FMVSS flammability | FMVSS302 | B | |
Fogging-G-value | ISO 6452 | 0.0 g |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ASTM D412/ISO 527 | 15500 kg/cm²(MPa)[Lb/in²] | |
Rockwell hardness | ASTM D785 | 100 | |
flexural modulus | ASTM D790/ISO 178 | 13500 kg/cm²(MPa)[Lb/in²] | |
Tensile modulus | ISO 527-2 | 15500 Mpa | |
tensile strength | ISO 527-2 | 182 Mpa | |
Tensile strain | ISO 527-2 | 2.0 % | |
Tensile creep modulus | ISO 899-1 | 15600 Mpa | |
ISO 899-1 | 13300 Mpa | ||
flexural modulus | ISO 178 | 13500 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179/1eU | 40 kJ/m² | |
ISO 179/1eU | 60 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface Resistivity | ASTM D257/IEC 60093 | 1.00E+14 Ω | |
dielectric constant | ASTM D150/IEC 60250 | 4.5 | |
ASTM D150/IEC 60250 | 4.4 | ||
volume resistivity | ASTM D257/IEC 60093 | 1.00E+13 Ω.cm | |
Surface Resistivity | IEC 60093 | 1E+14 ohms | |
volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
dielectric strength | IEC 60243-1 | 32 KV/mm | |
relative permittivity | IEC 60250 | 4.50 | |
IEC 60250 | 4.40 | ||
Dissipation Factor | IEC 60250 | 7E-03 | |
IEC 60250 | 0.011 | ||
Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
IEC 60112 | PLC 2 |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1690 | |
shrinkage rate | ASTM D955 | 0.85 % | |
Water absorption rate | ASTM D570/ISO 62 | 0.14 % | |
Ejection Temperature | 170 °C | ||
Melt volume flow rate | ISO 1133 | 2.50 cm3/10min | |
shrinkage rate | ISO 294-4 | 0.80 % | |
ISO 294-4 | 0.20 % | ||
Water absorption rate | ISO 62 | 0.62 % | |
ISO 62 | 0.14 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.