Material Description

Material Properties:High impact resistance
Application Areas:Fitness equipment｜Bottle cap｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Top out temperature			190 °C

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	80 kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	20 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	--
Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	20 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00 mm	ISO 3795	< 100 mm/min
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ISO 4589-2	20 %
FMVSS combustion rate		FMVSS 302	B

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	1800 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1 hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	> 50 %
tensile strength	50% Strain	ISO 527-2	49.0 Mpa
Tensile modulus		ISO 527-2	2000 Mpa

injection	Test Condition	Test Result
Mold Temperature, Optimum		80 °C
Maintain pressure		50.0 to 100 Mpa
Processing (melt) temperature		280 to 300 °C
Melt Temperature, Optimum		290 °C
Mold temperature		50 to 100 °C
drying temperature		80 °C
Drying time - hot air dryer		2.0 to 4.0 hr
Suggested maximum moisture content		0.20 %
Maintain pressure	Drying Recommended	yes
Hold Pressure Time		4.00 s/mm
Maximum Screw Tangential Speed		18 m/min

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ASTM E831	1.4E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.4E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	1.1E-4 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	157 °C
Vicat softening temperature		ISO 306/B50	205 °C
Glass transition temperature		ISO 11357-2	75.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	63.0 °C
Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.6E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ASTM E831	1.3E-4 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.3E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	1.1E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.3E-4 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Stickiness		ISO 307	130 cm³/g
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0 %
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.5 %
	Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	1.1 %
Shrinkage rate	Flow	ISO 294-4	1.8 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.4 %
density		ISO 1183	1.07 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 62631-3-2	-- ohms
Volume resistivity		IEC 62631-3-1	> 1.0E+13 ohms·m
Dielectric strength		IEC 60243-1	25 KV/mm
Relative permittivity	1 MHz	IEC 62631-2-1	3.30
Relative permittivity	Relative permittivity	100 Hz	IEC 62631-2-1	3.50
Dissipation factor	100 Hz	IEC 62631-2-1	5.0E-3
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.010
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.