POM/PTFE Iupital™ FL2010 MITSUBISHI ENGINEERING JAPAN
294
- Unit Price:US$ 19,644 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜Medium viscosity
- Application Areas:Electronic and Electrical Applications｜Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Not annealed | ISO 75-2/B | 154 °C | |
| 1.8MPa, Not annealed | ISO 75-2/A | 97.0 °C | |
| melting temperature | ISO 11357-3 | 166 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 60 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 7.5 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 6.10 cm3/10min |
| shrinkage rate | MD：3.00mm | 2.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.19 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | 1.00mm | IEC 60243-1 | 25 KV/mm |
| 3.00mm | IEC 60243-1 | 16 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2650 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 52.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 8.0 % |
| Nominal tensile fracture strain | ISO 527-2 | 18 % | |
| flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 77.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.