thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa	ISO 75-2	144	°C
Charpy Notched Impact Strength	23℃	ISO 179/1eA	2.5	kJ/m²
Impact strength of cantilever beam gap	23℃	ISO 180/1eU	2.5	kJ/m²
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.22	g/cm³
melt mass-flow rate	230℃, 2.16kg	ISO 1133	22	g/10min
Bending modulus, 2 mm/min		ISO 178	3800	Mpa
bending strength	2 mm/min	ISO 178	52	Mpa
Tensile modulus	1 mm/min	ISO 527-2	3800	Mpa
tensile strength	50 mm/min	ISO 527-2	30	Mpa
Tensile strain	50 mm/min，Break	ISO 527-2	3	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.