LCP LAPEROS® S475 VF2001 JAPAN POLYPLASTIC

233

Unit Price:US$ 10,323 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
110MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage｜High mobility｜heat-resisting｜Flame retardant｜enhance｜Glass fiber reinforced
Application Areas:Home appliance components｜Electrical applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	15 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Fracture bending strain		ISO 178	2.4 %
bending strength	23°C	ISO 178	180 Mpa
Bending modulus	23°C	ISO 178	12000 Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.8 %
tensile strength	Break	ISO 527-2/1A/5	135 Mpa
Tensile modulus		ISO 527-2/1A	12300 Mpa

injection	Test Condition	Test Method	Test Result
Mold temperature			80 to 120 °C
Injection speed			中等
Processing (melt) temperature			360 to 375 °C
Spray nozzle temperature			355 to 370 °C
Temperature at the front of the material cylinder			345 to 365 °C
Temperature in the middle of the barrel			340 to 360 °C
Temperature at the rear of the barrel			330 to 350 °C
Hopper temperature			20 to 40 °C
Suggested maximum moisture content			0.010 %
drying time			6.0 hr
drying temperature			150 °C
Back pressure			< 3.00 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-5 cm/cm/°C
Melting temperature		ISO 11357-3	350 °C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	213 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	305 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.0 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1 MHz	IEC 60250	8.0E-3
Relative permittivity	1 MHz	IEC 60250	3.70

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.