PC/PET XYLEX™  XL1339-78211 SABIC INNOVATIVE US

212
  • Unit Price:US$ 3,384 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    62MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High heat resistance
  • Application Areas:Automotive componentsElectronic and electrical components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet Compare

thermal performanceTest ConditionTest MethodTest Result
Heat Deflection Temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距ISO 75-2/Be125 °C
Heat Deflection Temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距ISO 75-2/Ae105 °C
vicat--ISO 306/A50140 °C
vicat--ISO 306/B50130 °C
vicat--ISO 306/B120135 °C
Linear coefficient of thermal expansion流动 : -30 到 30°CASTM D6967.6E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : -30 到 30°CASTM D6967.9E-5 cm/cm/°C
thermal conductivityASTM C1770.18 W/m/K
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA35 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA45 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Physical propertiesTest ConditionTest MethodTest Result
Melt volume flow rate265°C/1.2 kgISO 11334.00 cm3/10min
shrinkage rate流动内部方法0.50 - 0.80 %
shrinkage rate横向流动内部方法0.50 - 0.80 %
Water absorption rate24 hrASTM D5700.10 %
Water absorption rate平衡, 23°CASTM D5700.70 %
Water absorption rate平衡, 50% RHASTM D5700.20 %
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityASTM D257> 1.0E+15 ohms
volume resistivityASTM D257> 1.0E+14 ohms·cm
dielectric strength3.20 mm, in OilASTM D14917 KV/mm
dielectric constant60 HzASTM D1503.30
dielectric constant50 kHzASTM D1503.30
dielectric constant1 MHzASTM D1503.10
Dissipation Factor50 HzASTM D1502.0E-3
Dissipation Factor60 HzASTM D1502.0E-3
Dissipation Factor1 MHzASTM D1500.020
injectionTest ConditionTest MethodTest Result
drying temperature110 °C
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume50 to 80 %
Temperature at the rear of the barrel245 to 265 °C
Temperature in the middle of the barrel250 to 270 °C
Temperature at the front of the material cylinder255 to 275 °C
Spray nozzle temperature255 to 270 °C
Processing (melt) temperature260 to 275 °C
mold temperature65 to 90 °C
Back pressure0.300 to 0.700 Mpa
screw speed50 to 80 rpm
Exhaust hole depth0.013 to 0.020 mm
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6382090 Mpa
tensile strength屈服3ASTM D63849.0 Mpa
tensile strength屈服ISO 527-2/5055.0 Mpa
tensile strength断裂3ASTM D63849.0 Mpa
tensile strength断裂ISO 527-2/5040.0 Mpa
elongation屈服3ASTM D6385.0 %
elongation屈服ISO 527-2/505.0 %
elongation断裂3ASTM D638110 %
elongation断裂ISO 527-2/5070 %
flexural modulus50.0 mm 跨距4ASTM D7902090 Mpa
flexural modulus--5ISO 1782200 Mpa
bending strength--5,6ISO 17880.0 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79094.0 Mpa
Poisson's ratioASTM E1320.40
Taber abraser1000 Cycles, 1000 g, CS-17 转轮ASTM D104416.0 mg
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.