PA66 LATAMID 66 H2 G/25 V0 CT1 LATI ITALY

509

Unit Price:US$ 5,650 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜25%｜Filler by weight
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ASTM D2863	35	%
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	900	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.0mm	IEC 60695-2-13	900	°C
Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
UL flame retardant rating	3.0mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,90°C	ISO 527-2/5	3.8	%
	Tensile strain	Break,120°C	ISO 527-2/5	3.9	%
		Tensile strain	Break,150°C	ISO 527-2/5	4.2	%
			Tensile strain	Break,60°C	ISO 527-2/5	2.4	%
				Tensile strain	Break,23°C	ISO 527-2/5	2.1	%
					Tensile strain	Yield,150°C	ISO 527-2/5	3.7	%
					Tensile strain	Tensile strain	Yield,120°C	ISO 527-2/5	3.5	%
tensile strength	Break,150°C	ISO 527-2/5	50.0	Mpa
	tensile strength	Break,120°C	ISO 527-2/5	60.0	Mpa
		tensile strength	Break,90°C	ISO 527-2/5	75.0	Mpa
			tensile strength	Break,60°C	ISO 527-2/5	95.0	Mpa
				tensile strength	Break,23°C	ISO 527-2/5	135	Mpa
					tensile strength	Yield,150°C	ISO 527-2/5	50.0	Mpa
					tensile strength	tensile strength	Yield,120°C	ISO 527-2/5	60.0	Mpa
Tensile modulus	23°C	ISO 527-2/1	9200	Mpa
	Tensile modulus	60°C	ISO 527-2/1	7200	Mpa
		Tensile modulus	150°C	ISO 527-2/1	2200	Mpa
			Tensile modulus	120°C	ISO 527-2/1	3200	Mpa
			Tensile modulus	Tensile modulus	90°C	ISO 527-2/1	4800	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	8E-06	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	255	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	240	°C
	Hot deformation temperature	Hot deformation temperature	连续使用温度4		115	°C
Vicat softening temperature		ISO 306/B50	245	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:2.00mm	ISO 294-4	0.35-0.60	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	ISO 294-4	0.70-1.0	%
Water absorption rate	23°C,24hr	ISO 62	0.25	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
dimensional stability			21.0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shanghai Huibao/Huibai	US$ 7390 /MT

Supplier Join

Get App

Top

PA66 LATAMID 66 H2 G/25 V0 CT1 LATI ITALY