Material Properties:transparent｜Crystallization occurs at the water inlet or mold temperature too high｜Balanced mold temperature requirements｜No hot spots
Application Areas:Higher impact strength｜Can replace transparent ABS or some PC applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
combustibility	3.0mm	UL 94	V-2
Heat Deflection Temperature	1.82MPa(264PSi)	ASTM D-648	65 °C
Heat Deflection Temperature	Heat Deflection Temperature	0.45MPa(66PSi)	ASTM D-648	73 °C
vicat	1kg负荷	ASTM D-1525	85 °C

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate	230℃,5kg		15 g/10min

Other performance	Test Condition	Test Method	Test Result
intrinsic viscosity			0.72

Physical properties	Test Condition	Test Method	Test Result
transmittance		ASTM D-1003	91 %
Haze ratio		ASTM D-1003	0.3 %
shrinkage rate	3.2mm(0.125in)	ASTM D-955	0.002-0.006 in/in

mechanical properties	Test Condition	Test Method	Test Result
Tensile stress	屈服	ASTM D-638	6700/7700 psi
tensile strength	屈服	ASTM D-790	9700 psi
Rockwell hardness		ASTM D-785	105 R
Impact strength of cantilever beam gap	23℃/-40℃	ASTM D-256	7/1.1 ft-lb/in
Elongation at break		ASTM D-638	5/310 %
flexural modulus		ASTM D-790	2.75×105 psi

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.