thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa未退火	ISO 75-2/Bf	93.0 °C
	Heat Deflection Temperature	熔融温度		220-260 °C
	Heat Deflection Temperature	Heat Deflection Temperature	模具温度		10.0-30.0 °C

Other performance	Test Condition	Test Method	Test Result
injection speed			高
pressure holding			20.0-50.0 Mpa

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD	ISO 294-4	1.0 %
shrinkage rate	shrinkage rate	TD	ISO 294-4	2.0 %
melt mass-flow rate	230℃/2.16Kg	ISO 1133	25 g/10min
density		ISO 1183	0.910 g/cm³

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	屈服伸长率	ISO 527-2	11 %
Tensile modulus	1mm/min，23°C	ISO 527-2	1400 Mpa
tensile strength	屈服，50mm/min，23°C	ISO 527-2	33.0 Mpa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	穿刺能量	ISO 6603-2	40.0 J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.