PC LEXAN™  EXL1132T NA8A005T SABIC INNOVATIVE NANSHA

159
  • Unit Price:US$ 3,153 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    23MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low temperature resistanceEasy to processHigh mobilityUV resistance
  • Application Areas:Household appliancesAutomotive sectorElectronic fieldElectrical field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet Compare

hardnessTest ConditionTest MethodTest Result
ball-indentation hardnessH358/30ISO 2039-195.0 Mpa
Rockwell hardnessL 计秤ISO 2039-289
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMD:-40到40°CASTME8317.2E-05 cm/cm/°C
Linear coefficient of thermal expansionMD:23到80°CISO 11359-27.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:-40到40°CASTME8317.6E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:23to80°CISO 11359-27.5E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
RTI StrUL 746125 °C
Heat Deflection Temperature0.45MPa,未退火,3.20mmASTM D648137 °C
Heat Deflection Temperature0.45MPa,AnnealedISO 75-2/Be136 °C
Heat Deflection Temperature1.8MPa,未退火,3.20mmASTM D648124 °C
Heat Deflection Temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae125 °C
vicatASTM D152511144 °C
vicat--ISO 306/B50144 °C
vicat--ISO 306/B120145 °C
ball-indentation hardness125°CIEC 60695-10-2Pass
Heat Deflection Temperature1.8 MPa, 未退火, 3.20 mmASTM D648121 °C
Heat Deflection Temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9ISO 75-2/Af116 °C
vicat--ASTM D152510138 °C
vicat--ISO 306/B120139 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansion流动 : -40 到 95°CASTM E8317.5E-5 cm/cm/°C
Linear coefficient of thermal expansion流动 : 23 到 80°CISO 11359-27.5E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : -40 到 95°CASTM E8317.6E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-27.6E-5 cm/cm/°C
RTI ElecUL 746130 °C
RTIUL 746130 °C
optical performance Test ConditionTest MethodTest Result
transmissivity2540 µmASTM D100382.0 %
Haze ratio2540 µmASTM D10033.0 %
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index1.0mmIEC 60695-2-12850 °C
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13875 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13875 °C
Limiting Oxygen IndexISO 4589-232 %
UL flame retardant rating1.5 mmUL 94HB
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13850 °C
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA25 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A20 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A55 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376369.6 J
Charpy Notched Impact Strength-30°CISO 179/1eA45 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376374.0 J
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123817 g/10min
Melt volume flow rate300°C/1.2kgISO 113316.0 cm3/10min
shrinkage rateMD:3.20mm内部方法0.40-0.80 %
shrinkage rateTD:3.20mm内部方法0.40-0.80 %
Water absorption rate饱和,23°CISO 620.35 %
Water absorption rate平衡,23°C,50%RHISO 620.15 %
melt mass-flow rate300°C/1.2 kgASTM D123820 g/10 min
Melt volume flow rate300°C/1.2 kgISO 113319.0 cm3/10min
shrinkage rate流动 : 3.20 mm内部方法0.40 - 0.80 %
shrinkage rate横向流动 : 3.20 mm内部方法0.40 - 0.80 %
Water absorption rate饱和, 23°CISO 620.12 %
Water absorption rate平衡, 23°C, 50% RHISO 620.090 %
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityASTM D257> 1.0E+15 ohms
volume resistivityASTM D257> 1.0E+15 ohms·cm
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6382280 Mpa
Tensile modulusISO 527-2/12150 Mpa
tensile strength屈服ASTM D63858.1 Mpa
tensile strength屈服ISO 527-2/5057.0 Mpa
tensile strength断裂ASTM D63858.7 Mpa
tensile strength断裂ISO 527-2/5055.0 Mpa
elongation屈服ASTM D6385.8 %
Tensile strain屈服ISO 527-2/505.0 %
elongation断裂ASTM D638110 %
Tensile strain断裂ISO 527-2/50100 %
flexural modulus50.0mm跨距ASTM D7902320 Mpa
flexural modulusISO 1782240 Mpa
bending strengthISO 17885.0 Mpa
bending strength屈服,50.0mm跨距ASTM D79095.1 Mpa
Tensile modulus--2ASTM D6382260 Mpa
Tensile modulus--ISO 527-2/12340 Mpa
tensile strength屈服3ASTM D63858.0 Mpa
tensile strength屈服ISO 527-2/5057.0 Mpa
tensile strength断裂3ASTM D63857.0 Mpa
tensile strength断裂ISO 527-2/5056.0 Mpa
elongation屈服3ASTM D6385.7 %
elongation屈服ISO 527-2/505.4 %
elongation断裂3ASTM D638120 %
elongation断裂ISO 527-2/50120 %
flexural modulus50.0 mm 跨距4ASTM D7902240 Mpa
flexural modulus--5ISO 1782140 Mpa
bending strength--5,6ISO 17889.0 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79094.0 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.