PC Makrolon® 8025 COVESTRO GERMANY

273

Unit Price:US$ 3,472 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
64MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜Filler: Glass fiber with embossing｜20% filler by weight
Application Areas:Fiber grade
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	3300 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	2800 N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	20.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	10.0 J
Impact strength of cantilever beam gap	23°C,CompleteBreak	ISO 7391	12 kJ/m²
Impact strength of simply supported beam without notch	23°C,Complete Break	ISO 179/1eU	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO 179/1eU	65 kJ/m²
Charpy Notched Impact Strength	23°C,CompleteBreak	ISO 7391	12 kJ/m²
Impact strength of simply supported beam without notch	-60°C,CompleteBreak	ISO 179/1eU	65 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	6.0mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-2
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
Extreme Oxygen Index		ISO 4589-2	32 %
Burning wire flammability index	0.75mm	IEC 60695-2-12	800 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C
			Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
			Burning wire flammability index	Burning wire flammability index	4.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	875 °C
Needle flame test	MethodF:2.00mm	IEC 60695-11-5	2.0 min
Needle flame test	Needle flame test	MethodF:3.00mm	IEC 60695-11-5	2.0 min
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN 53438-1,-3	K1.F1
Burning rate - US-FMVSS	>1.00mm	ISO 3795	passed
Needle flame test	MethodK:1.50mm	IEC 60695-11-5	1.0 min
	Needle flame test	MethodK:2.00mm	IEC 60695-11-5	1.0 min
	Needle flame test	Needle flame test	MethodK:3.00mm	IEC 60695-11-5	2.0 min
FlashIgnitionTemperature		ASTM D1929	470 °C
Needle flame test	MethodF:1.50mm	IEC 60695-11-5	2.0 min
SelfIgnition		ASTM D1929	550 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2/5	6.5 %
Tensile strain	Tensile strain	Yield,23°C	ISO 527-2/50	3.5 %
Tensile creep modulus	1hr	ISO 899-1	3700 Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	3500 Mpa
Bending modulus	23°C	ISO 178	3700 Mpa
bending strength	3.5%Strain,23°C	ISO 178	95.0 Mpa
bending strength	bending strength	23°C	ISO 178	100 Mpa
Bending strain	23°C	ISO 178	5.4 %
Tensile modulus	23°C	ISO 527-2/1	4000 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	58.0 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/5	50.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	134 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141 °C
Vicat softening temperature	--	ISO 306/B50	146 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	147 °C
Ball Pressure Test	137°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	5.5E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.23 W/m/K
RTI Elec	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
RTI Str	1.5mm	UL 746	125 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ISO 1133	6.5 g/10min
Apparent density		ISO 60	0.69 g/cm³
density	23°C	ISO 1183	1.34 g/cm³
Shrinkage rate	MD:2.00mm3	ISO 294-4	0.55 %
Water absorption rate	Saturation,23°C	ISO 62	0.24 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	TD	ISO 2577	0.30-0.45 %
	Shrinkage rate	MD	ISO 2577	0.30-0.45 %
	Shrinkage rate	Shrinkage rate	TD:2.00mm3	ISO 294-4	0.35 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	1E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.30
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.30
Dielectric strength	23°C,1.00mm	IEC 60243-1	36 KV/mm
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Surface resistivity		IEC 60093	1E+16 ohms

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	136 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 8025 COVESTRO GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet