ABS Toyolac® 100-322 TORAY MALAYSIA
235
- Unit Price:US$ 1,941 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:55MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜High impact resistance
- Application Areas:household electrical appliances｜Electronic and electrical components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 88.0 °C | |
| 1.8MPa, Unanealed, 12.7mm | ASTM D648 | 93.0 °C | |
| 1.8MPa, Not annealed | ISO 75-2/A | 83.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.4E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.15 W/m/K |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 140 J/m |
| -30°C,12.7mm | ASTM D256 | 120 J/m | |
| 0°C,3.20mm | ASTM D256 | 200 J/m | |
| 0°C,12.7mm | ASTM D256 | 180 J/m | |
| 23°C,3.20mm | ASTM D256 | 270 J/m | |
| 23°C,12.7mm | ASTM D256 | 230 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 1.04 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 15 g/10min |
| shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >1.0E+16 ohms | |
| volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
| dielectric strength | ASTM D149 | 23 KV/mm | |
| dielectric constant | 1kHz | ASTM D150 | 3.10 |
| Dissipation Factor | 1kHz | ASTM D150 | 6.6E-03 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ASTM D790 | 2280 Mpa | |
| --4 | ASTM D790 | 74.0 Mpa | |
| --5 | ISO 178 | 78.0 Mpa | |
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| yield | ASTM D638 | 48.0 Mpa | |
| ISO 527-2/50 | 51.0 Mpa | ||
| fracture | ASTM D638 | 48 % | |
| ISO 527-2/50 | >10 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.