PC PANLITE® L-1225L BK TEIJIN JAPAN
219
- Unit Price:US$ 2,859 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Flame retardant
- Application Areas:Electrical appliances｜Electrical field｜Electronic field｜Application in the automotive field｜Car headlights
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 115 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 136 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 123 °C | |
| vicat | ISO 306/B50 | 142 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.585 | |
| transmissivity | 3000µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 2.1mm | UL 94 | HB |
| 0.40mm | UL 94 | V-2 | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 825 °C |
| 3.2mm | IEC 60695-2-12 | 875 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 850 °C |
| 3.2mm | IEC 60695-2-13 | 875 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 53 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.10 |
| 1MHz | IEC 60250 | 3.00 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 9E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.20 g/cm³ | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 25.0 cm3/10min |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.50-0.70 % |
| MD:4.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | >50 % | |
| flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 95.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.