impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	19	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	1600	Mpa
tensile strength	Yield	ISO 527-2	39.0	Mpa
Tensile strain	Yield	ISO 527-2	12	%
Nominal tensile fracture strain		ISO 527-2	>100	%
Bending modulus		ISO 178	1400	Mpa
bending strength		ISO 178	48.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	76.0	°C
Melting temperature		ISO 11357-3	166	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.35	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	6.0	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	5.20	cm3/10min
Shrinkage rate	MD：3.00mm		1.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.