PC SABIC® 1803R SABIC INNOVATIVE SHANGHAI
237
- Unit Price:US$ 3,163 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:54MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜High temperature resistance｜enhance｜Thermal stability｜Flame retardant
- Application Areas:Automotive sector｜Laptop case｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness (Rockwell R) | ASTM D785 | 120 | |
| ISO 2039-2 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| -40 to 95 ° C | ASTME831 | 7E-05 cm/cm/°C | |
| 23 to 80 ° C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| thermal conductivity | DENKA Method | 0.20 W/m/K |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0to90.0 % |
| Haze ratio | 2540µm | ASTM D1003 | <0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 700 J/m | |
| -30°C | ISO 180/1A | 12 kJ/m² | |
| 23°C | ISO 180/1A | 70 kJ/m² | |
| ASTMD4812 | 无断裂 | ||
| -30°C | ISO 180/1U | 无断裂 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 17.0 cm3/10min |
| shrinkage rate | MD：--1 | 内部方法 | 0.50-0.70 % |
| MD：3.20mm | 内部方法 | 0.50-0.70 % | |
| Saturation, 23 ° C | ISO 62 | 0.35 % | |
| Balance, 23 ° C | ASTM D570 | 0.35 % | |
| density | ASTMD792 | 1.20 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm | ASTM D2863 | 27 KV/mm |
| dielectric constant | 60Hz | ASTMD150 | 3.00 |
| 1MHz | ASTMD150 | 3.00 | |
| Dissipation Factor | 60Hz | ASTMD150 | 1E-03 |
| 1MHz | ASTMD150 | 0.010 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --2 | ASTM D638 | 2350 Mpa | |
| yield | ASTM D638 | 63.0 Mpa | |
| ISO 527-2/50 | 63.0 Mpa | ||
| ASTM D638 | 6.0 % | ||
| ISO 527-2/50 | 6.0 % | ||
| fracture | ASTM D638 | >70 % | |
| ISO 527-2/50 | >70 % | ||
| 50.0mm span | ASTM D790 | 2300 Mpa | |
| --7 | ISO 178 | 2300 Mpa | |
| --8 | ISO 178 | 90.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 90.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.