PEI

PEI 1000-1000MC SABIC INNOVATIVE US

299

Unit Price:US$ 23,129 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C	ASTM D3029	36.6 J
Impact strength of cantilever beam gap	3.20mm	ASTM D256	1300 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D4812	1300 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	53 J/m

flammability	Test Condition	Test Method	Test Result
NBSSmokeDensity-Flaming,Ds,4min		ASTME662	0.700
Extreme Oxygen Index		ASTM D2863	47 %
UL flame retardant rating	3.0mm	UL 94	5VA
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.40mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	60 %
Bending modulus	100mmSpan	ASTM D790	3520 Mpa
elongation	Yield	ASTM D638	7.0 %
tensile strength	Yield	ASTM D638	110 Mpa
Tensile modulus		ASTM D638	3590 Mpa
Poisson's ratio		ASTM D638	0.36
bending strength	Yield,100mmSpan	ASTM D790	165 Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	10.0 mg

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	201 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	210 °C
Vicat softening temperature		ASTM D15255	219 °C
Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	5.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-20to150°C	ASTME831	5.4E-05 cm/cm/°C
thermal conductivity		ASTMC177	0.22 W/m/K
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	170 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C	ASTM D570	1.3 %
Water absorption rate	Water absorption rate	24hr	ASTM D570	0.25 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
melt mass-flow rate	337°C/6.6kg	ASTM D1238	9.0 g/10min
density		ASTM D792	1.27 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 1
Volume resistivity		ASTM D257	1E+17 ohms·cm
Dielectric strength	1.60mm,inAir	ASTM D149	33 KV/mm
	Dielectric strength	1.60mm,in Oil	ASTM D149	28 KV/mm
	Dielectric strength	Dielectric strength	3.20mm,in Oil	ASTM D149	20 KV/mm
Dielectric constant	100Hz	ASTM D150	3.15
Dielectric constant	Dielectric constant	1kHz	ASTM D150	3.15
Dissipation factor	100Hz	ASTM D150	1.5E-03
	Dissipation factor	1kHz	ASTM D150	1.2E-03
	Dissipation factor	Dissipation factor	2.45GHz	ASTM D150	2.5E-03
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	109

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI 1000-1000MC SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet