thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	288 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	285 °C
melting temperature		ISO 11357-3	290 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	3.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	3.0E-5 cm/cm/°C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	ISO 294-4	0.90 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	0.40 %
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	1.6 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2	16000 Mpa
	Tensile modulus	160°C	ISO 527-2	8300 Mpa
	Tensile modulus	Tensile modulus	200°C	ISO 527-2	7600 Mpa
tensile strength	断裂	ISO 527-2	235 Mpa
	tensile strength	断裂, 160°C	ISO 527-2	120 Mpa
	tensile strength	tensile strength	断裂, 200°C	ISO 527-2	105 Mpa
Tensile strain	断裂	ISO 527-2	2.2 %
	Tensile strain	断裂, 160°C	ISO 527-2	3.4 %
	Tensile strain	Tensile strain	断裂, 200°C	ISO 527-2	3.5 %
flexural modulus		ISO 178	12500 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.